Nickel Alloy X Bar

Alloy X is an austenitic nickel base alloy containing approximately 22 percent chromium for outstanding resistance to oxidation at high temperatures. In addition, the alloy, which is solid solution strengthened, possesses exceptional strength at elevated temperatures. The alloy has good high temperature and stress rupture properties above 1450°F and can be used for applications up to 2200°F. In addition Alloy X contains high levels of nickel and molybdenum providing good levels of corrosion resistance similar to high nickel alloys more customarily used in corrosion applications.

Specific Gravity

8.22 g/cm3

Typical Applications

Related Specifications

Gas Turbine engine components

AMS 5798

AMS 5754

UNS N06002

ASTM B572

Chemical Composition (Wt %)

	Cr	Mo	Co	W	Al	Ti	B	C	Fe	Mn	Si	P	S	Cu	Ni
Min	20.5	8	0.5	0.2	–	–	–	0.05	17	–	–	–	–	–	–
Max	23	10	2.5	1.0	0.5	0.15	0.01	0.15	20	1.0	1.0	0.04	0.03	0.5	Bal

Typcial Mechanical Properties

	0.2% Proof Stress	Tensile Strength	Elongation
	MPA	MPA	MPA
Temp deg f
70	379	765	44
1000	284	702	49
1200	276	654	54
1400	268	529	53
1600	221	355	58